1.4305 (303)


1.4305 (303)

X10CrNiS 18-9

SUS303

S30300

Stainless steel grade 303(1.4305) is the most readily machineable of all the austenitic grades of stainless steel.
The machineable nature of grade 303 is due to the presence of Sulphur in the steel composition. Whilst the Sulphur improves machining, it also causes a decrease in the corrosion resistance and a slight lowering of the toughness. The corrosion resistance of type 303 is lower than that for 304. The toughness is still excellent as with other austenitic grades.

Chemical Composition

Grade C Si Mn S P Cr Ni Mo
303 ≤0.15 ≤1.0 ≤2.0 ≥0.15 ≤0.2 17.0-19.0 8.0-10.0 ≤0.6
Corrosion Resistance

Sulphur additions to the composition act as initiation sites for pitting corrosion. This decreases the corrosion resistance of 303 stainless steel to less than that for 304. However. corrosion resistance remains good in mild environments.

In chloride containing environments over 60°C, 303 stainless steel is subject to pitting and crevice corrosion. Grade 303 stainless is not suitable for use in marine environments.

Heat Resistance

Grade 303 stainless steel has good resistance to oxidation when intermittently exposed to temperature up to 760°C temperatures. It also has good oxidation resistance in continuous service to 870°C. This, however, is not recommended as 303 is sensitive to carbide precipitation with continuous use at 425-860°C.

Machinability

Grade 303 stainless steel has excellent machinability. Machining can be enhanced by adhering to the following rules:

Cutting edges must be kept sharp. Dull edges cause excess work hardening.

Cuts should be light but deep enough to prevent work hardening by riding on the surface of the material.

Chip breakers should be employed to assist in ensuring swarf remains clear of the work

Low thermal conductivity of austenitic alloys results in heat concentrating at the cutting edges. This means coolants and lubricants are necessary and must be used in large quantities.

Heat Treatment

Grade 303 stainlesssteel cannot be hardened by heat treatment.

Solution treatment or annealing can be done by rapid cooling after heating to 1010-1120°C.

Weldability

The sulphur addition present in 303 stainless steel results in poor weldability. If 303 must be welded the recommended filler rods or electrodes are grades 308L and 309 stainless steels. For maximum corrosion resistance, the welds must be annealed.